在一次性餐具的注塑成型過(guò)程中，有三個(gè)過(guò)渡階段：一是一次性餐具材料沒(méi)有進(jìn)入料筒時(shí)的顆粒狀態(tài)；二是塑料在料筒內(nèi)流動(dòng)達(dá)到“二次極”狀態(tài)；三是一次性餐具材料通過(guò)一次性餐具模具澆注系統(tǒng)的流動(dòng)和冷卻。在每個(gè)階段，都必須有特定的工藝成型條件。

In the injection molding process of disposable tableware, there are three transitional stages: one is the particle state when the disposable tableware material does not enter the barrel; Second, the plastic flow in the barrel reaches the "secondary pole" state; The third is the flow and cooling of disposable tableware materials through the pouring system of disposable tableware mold. At each stage, there must be specific process forming conditions.

顆粒狀態(tài)：

Particle status:

預(yù)熱干燥：

Preheating and drying:

原料預(yù)熱干燥1.5-2min，料溫升80C°-100c°。原因是原料中的水分含量往往過(guò)高。如果直接放入桶中，產(chǎn)品表面會(huì)變暗，顏色不均勻，表面起泡。但預(yù)熱時(shí)間要適當(dāng)，溫度不宜過(guò)高。溫度過(guò)高，產(chǎn)品表面會(huì)出現(xiàn)焦斑；如果預(yù)熱溫度過(guò)高或預(yù)熱時(shí)間過(guò)長(zhǎng)，產(chǎn)品表面顏色會(huì)不均勻。

The raw materials shall be preheated and dried for 1.5-2min, and the material temperature shall rise to 80C ° -100c °. The reason is that the moisture content in raw materials is often too high. If the product is directly put into the barrel, the surface of the product will become dark, the color will be uneven, and the surface will blister. However, the preheating time should be appropriate and the temperature should not be too high. If the temperature is too high, the product surface will appear coke spots; If the preheating temperature is too high or the preheating time is too long, the product surface color will be uneven.

進(jìn)料測(cè)量：

Incoming measurement:

進(jìn)料量要準(zhǔn)確。原料過(guò)多，產(chǎn)品毛邊過(guò)多，難以清洗；原料太少，成型壓力不足，產(chǎn)品不能完全固化。

The feeding amount shall be accurate. There are too many raw materials and too many rough edges, which are difficult to clean; Too few raw materials, insufficient forming pressure, and the product can not be fully cured.

融合狀態(tài)：

Fusion status:

控制成型溫度和壓力：

Control forming temperature and pressure:

根據(jù)一次性餐具材料佳成型條件的要求，一次性餐具模具的成型溫度應(yīng)控制在150-220℃。初始?jí)毫刂圃?0mpa-90mpa之間，加壓時(shí)間1-5s。如果原料溫度過(guò)高，容易造成產(chǎn)品表面有焦斑，產(chǎn)品顏色不均勻；初壓時(shí)間過(guò)長(zhǎng)，產(chǎn)品表面會(huì)松散；不合適的成型溫度和壓力會(huì)導(dǎo)致塑料流動(dòng)性能變差。

According to the requirements of good molding conditions for disposable tableware materials, the molding temperature of disposable tableware mold should be controlled at 150-220 ℃. The initial pressure is controlled between 70mpa-90mpa and the pressurization time is 1-5s. If the raw material temperature is too high, it is easy to cause scorch spots on the product surface and uneven product color; If the initial pressing time is too long, the product surface will be loose; Improper molding temperature and pressure will lead to poor plastic flow performance.

排氣狀態(tài)：

Exhaust status:

一次性環(huán)保餐具成型過(guò)程中會(huì)產(chǎn)生冷凝水和揮發(fā)性氣體，所以成型過(guò)程中應(yīng)進(jìn)行排氣，防止制品表面松動(dòng)。通常，放氣的次數(shù)和時(shí)間由經(jīng)驗(yàn)決定，放氣動(dòng)作應(yīng)盡可能快。只要及時(shí)卸壓，恢復(fù)原來(lái)的壓力，放氣操作就完成了。餐具的結(jié)構(gòu)并不復(fù)雜，所以不需要從一次性餐具模具的角度考慮排氣結(jié)構(gòu)。

Condensing water and volatile gas will be produced during the molding process of disposable environment-friendly tableware, so exhaust should be carried out during the molding process to prevent the product surface from loosening. Generally, the number and time of bleeding are determined by experience, and the bleeding action should be as fast as possible. As long as the pressure is relieved in time and the original pressure is restored, the bleeding operation is completed. The structure of tableware is not complicated, so it is not necessary to consider the exhaust structure from the perspective of disposable tableware mold.

模流和冷卻設(shè)置：

Mold flow and cooling settings:

固化階段：

Curing stage:

排氣后立即合模，壓力升70-90mpa約70s。在這個(gè)階段，固化時(shí)間要足夠長(zhǎng)，否則產(chǎn)品表面會(huì)變黑。

Close the mold immediately after the exhaust, and the pressure rises to 70-90mpa for about 70s. At this stage, the curing time should be long enough, otherwise the product surface will turn black.

脫模：

Demoulding:

固化后對(duì)產(chǎn)品進(jìn)行風(fēng)冷，噴涂機(jī)構(gòu)對(duì)產(chǎn)品進(jìn)行噴涂。

After curing, the product shall be air cooled, and the spraying mechanism shall spray the product.

脫模后的處理：

Treatment after demoulding:

我們做的是餐具，所以產(chǎn)品成型后要在一次性餐具模具中加熱120℃以上30-60分鐘，進(jìn)一步凝固。后進(jìn)行閃光打磨，完成一次性環(huán)保餐具的制作。

What we do is tableware, so after the product is formed, it should be heated in the disposable tableware mold above 120 ℃ for 30-60 minutes to further solidify. After that, flash polishing is carried out to complete the production of disposable environment-friendly tableware.

以上就是今天為大家分享的關(guān)于問(wèn)題的相關(guān)內(nèi)容，希望對(duì)大家能有所幫助，想要了解更多內(nèi)容可以電話聯(lián)系我們或者關(guān)注我們的網(wǎng)站http://m.88dyk.com。

The above is the relevant content about the problem shared for you today. I hope it can help you. If you want to know more, you can contact us by phone or follow our website http://m.88dyk.com 。